DESCRIPTION        Finncoatings®color on the highest level
Solvent free TEMAFLOOR 4000 grinding screed is prepared by adding sand to TEMAFLOOR 400 epoxy varnish mixture.


PRODUCT FEATURES
   
For new and old concrete floors exposed to heavy mechanical and moderate chemical stress in production facilities, e.g. in wood, chemical and food industries.


RECOMMENDED USES  
      Finncoatings®color on the highest level
Due to good impact resistance suitable for e.g. loading platforms, repair shops and market floors. Recommended also for floors subjected to steam and heat; e.g. in institutional kitchens and dairies.


TECHNICAL DATA


Features    
Withstands heavy wear. Resistance to chemicals is given case by case. Withstands + 110 ºC dry heat and + 60 ºC in immersion. Reaction to fire: CFL-s1according to standard EN 13501-1.

Colour Range
   
The colour of the screed is determined by the sand used.


Gloss groups
     Finncoatings®color on the highest level 
Full-gloss


Coverage     


For a flat substrate:
1 mm layer: 1 litre ready for use screed / m2
5 mm layer: 5 litres ready for use screed / m2

Practical coverage depends on the evenness of the substrate.

 

Mixing ratio    

TEMAFLOOR 400 mixture:

Base 3 parts by volume 008 4403
Hardener 1 part by volume 008 4408   Finncoatings®color on the highest level

Screed film thickness 2 - 10 mm:
1 part by volume TEMAFLOOR 400 mixture
6 - 8 parts by volume of filler sand, e.g. grain size of 1.0 - 1.8 mm

Note! The amount of the filler and the grain size depends on the object.

Application method
       Finncoatings®color on the highest level

By adjustable trowel, serrated trowel, float, levelling trowel and screed box.

Pot-life (+23°C)     30 - 45 minutes on substrate, 15 - 30 minutes in the mixing container.
Drying time at 23°C and 50% relative air humidity     Dust dry after 6 hours
Light trucking after 24 hours
Recoatable after 16–24 hours
Fully cured after 7 days

At lower temperature the curing process will last longer.

Solids volume
   

approx. 100 volume %

Density     1.8 - 2.1 kg / l (mixture), depending on the grain size and the amount of sand.

APPLICATION DETAILS

Application conditions        Finncoatings®color on the highest level
The relative humidity of the concrete should not exceed 97%. The temperature of the ambient air, surface or coating should not fall below +15ºC during either application or drying. Relative humidity of air should not exceed 80%.


Preparation
   

New concrete
   Finncoatings®color on the highest level
Remove laitance by power grinding, vacuum grit blasting or hydrochloric acid etching. Choose the method best suited for the premises. After grinding remove dust carefully with a vacuum cleaner. Hydrochloric acid etching is carried out with diluted hydrochloric acid (1 part concentrated hydrochloric acid, 4 parts water). Rinse with plenty of water. Dry the floor.

Old concrete
Remove all grease, oil, chemicals and other impurities by MAALIPESU detergent. Remove old peeling paint layer by grinding, milling or vacuum grit blasting. Choose the method best suited for the premises. Clean out pot-holes removing all loose friable material. Open cracks with e.g. an abrasive tool. Remove loose material and dust.

Cementitious levelling screed
Check compatibility with the levelling screed manufacturer.

Priming
   
Prime using 10–30% with Thinner 1029 thinned TEMAFLOOR 400 epoxy varnish. Pour the varnish mixture onto the floor and apply as much as is needed to impregnate the concrete surface. If necessary, repeat priming to get a non-porous surface. Subsequent treatment can be carried out after 2 hours using "wet-on-wet" technique.

Scatter sand of grain size 0.5–1.2 mm on the fresh primer coat to ensure the screed adhesion and prohibit gliding of the screed.

Diluting
   
Do not thin TEMAFLOOR 4000 grinding screed.


Screeding
   
Pour the screed mixture onto the floor. If a thin layer is required, apply by an adjustable trowel to the desired screed thickness. Thick layers are applied by a screed box or by a straight-edge and suitable laths to gauge the required thickness. Knead the screeded surface by hands or use a suitable lightweight floating machine.


Overcoating
       Finncoatings®color on the highest level
Overcoating can be carried out after 16–24 hours using unthinned TEMAFLOOR 400 epoxy varnish. If the surface is not overcoated within 24 hrs, it should be abraded. Pour the varnish mixture onto the floor, spread with a rubber trowel and level with a roller.


Mixing of components
   
Mix the correct proportions of base and hardener thoroughly (approx. 2 minutes) by using a hand drill with a paddle, concrete mixer or power mixer. Add filler to the varnish mixture by mixing carefully at the same time. Insufficient mixing or incorrect mixing ratio will result in uneven drying of the surface, weaken the properties of the screed and risk the success of the application.


Cleaning of tools  
  
Thinner 006 1029.


EU VOC 2004/42/EC-limit value     VOC 2004/42/EC (cat A/j) 500 g/l (2010)
Temafloor 4000: max. VOC < 500 g/l

 

The European harmonized productstandard EN 13813 defines the requirements for Screed materials and floor screeds, including synthetic resin screeds.This product is tested and CE-labelled in accordance with the tables ZA.1.5 and ZA.3.3 in the appendix ZA.3.

 

CE logo
 
Tikkurila Oyj
Kuninkaalantie 1
FI-01301 VANTAA
11
TIK-8400-5012b
EN 13813
Coating/Screed
Abrasion resistance
RWA 10
Chemical resistance
CR 1, 2, 5, 6b, 7…8, 10…12, 14 (Class 2)
   
Release of corrosive substances
SR
Impact resistance
IR4
Sound insulation
NPD
Sound absorption
NPD
Thermal resistance
NPD
Reaction to fire
Cfl
Water permeability
NPD
Adhesion
Adhesion strength by pull off test: B 2.0
   

 

 The European harmonized productstandard EN 1504-2 defines the requirements for surface protection systems for concrete.This product is tested and CE-labelled in accordance with the tables 1d, 1f and 1g in the
appendix ZA.

 

 

 

CE logo
0809

 

 

 

Tikkurila Oyj
Kuninkaalantie 1
FI-01301 VANTAA
13
TIK-8400-5012a
EN 1504-2
Coating
Abrasion resistance
< 3000 mg
Resistance to severe chemical attack
Class II
   
Permeability to CO2
CO2sD > 50 m
Impact resistance
Class I: ≥ 4 Nm
Permeability to water vapour
w < 0,1 kg/m² ∙ h0,5
Adhesion
Adhesion strength by pull off test:≥ 2,0 N/mm²
Reaction to fire
Cfl-s1

 

The above information is not intended to be exhaustive or complete. The information is based on laboratory tests and practical experience, and it is given to the best of our knowledge. The quality of the product is ensured by our operational system, based on the requirements of ISO 9001 and ISO 14001. As manufacturer we cannot control the conditions under which the product is being used or the many factors that have an effect on the use and application of the product. We disclaim liability for any damages caused by using the product against our instructions or for inappropriate purposes. We reserve the right to change the given information unilaterally without notice. The product is intended for professional use only and shall only be used by professionals who have sufficient knowledge and expertise on the proper use of the product. The information above is advisory only. To the extent permitted by applicable law, we shall not approve of any liability for the conditions under which the product is being used or for the use or application of the product. In case you intend to use the product for any other purpose than that recommended in this document without first getting our written confirmation on the suitability for the intended use, such use takes place at your own risk.

 

  Finncoatings® Color on the highest level

 

Finncoatings  
Heidelberger Straße 8
74858 Aglasterhausen-Germany

 

Tel. + 49 (0)6262 917095
Fax  + 49 (0)6262 917791

www.finncoatings.com
Mail. This email address is being protected from spambots. You need JavaScript enabled to view it.